[논문]CASTING DEFECTS AND THE FATIGUE BEHAVIOUR OF AN ALUMINIUM CASTING ALLOY

Couper, M. J.; Neeson, A. E.; Griffiths, J. R.

doi:10.1111/j.1460-2695.1990.tb00594.x

CASTING DEFECTS AND THE FATIGUE BEHAVIOUR OF AN ALUMINIUM CASTING ALLOY

Fatigue & fracture of engineering materials & structures, v.13 no.3, 1990년, pp.213 - 227

Couper, M. J. (Department of Materials Engineering, Monash University, Clayton, Victoria 3168, Australia) , Neeson, A. E. (Department of Materials Engineering, Monash University, Clayton, Victoria 3168, Australia) , Griffiths, J. R. (Department of Materials Engineering, Monash University, Clayton, Victoria 3168, Australia)

Abstract ▼ AI-Helper

Abstract— The fatigue properties of un‐notched polished specimens of an aluminium casting alloy have been measured for various heat‐treatment conditions and at various mean stresses. The relation between fatigue life and alternating stress is insensitive to heat‐treatment and, apparently, to mean stress. It was observed that failure initiated at interdendritic shrinkage defects: evidence of classical crack initiation from persistent slip bands was also seen but such cracks, being less severe than the casting defects, never caused failure. A fracture mechanics analysis for the growth of fatigue cracks from the pores is described. It shows that the fatigue life can be quantitatively predicted from a knowledge of the size of casting defects: in particular it explains the lack of effect of heat‐treatment and the apparent absence of a mean stress effect is shown to be caused by the variation in size of maximum defect present among the specimens tested. It is shown that reducing the size of shrinkage defects will increase the life, but only up to the stage at which initiation from persistent slip bands becomes operative.

참고문헌 (22)

1 D. C. Jenkinson and L. M. Hogan ( 1975 ) The modification of aluminium‐silicon alloys with strontium . J. Cryst. Growth 28 , 171 – 187 .

상세보기
2 D. S. Saunders , J. R. Griffiths and B. A. Parker ( 1975 ) The fracture toughness of an aluminium casting alloy . J. Aust. Inst. Metals 20 , 33 – 38 .
3 R. W. Coade ( 1980 ) The effect of second phase particles on the ductile failure of an Al‐Mg‐Si casting alloy . Ph.D. thesis , Monash University , Clayton , Australia .
4 M. J. Couper ( 1982 ) Fatigue of an Al‐Mg‐Si casting alloy . Ph.D. thesis , Monash University , Clayton , Australia .
5 L. P. Pook , A. G. Greenan , M. S. Found and W. J. Jackson ( 1980 ) Tests to determine the fatigue strength of steel castings containing shrinkage . J. Res. Steel Castings Res. Trade Assoc. 49 , 28 – 35 .
6 B. Östensso ( 1973 ) Influence of microshrinkage cavities on the endurance limit of nodular cast iron . J. Iron Steel Inst. 211 , 628 – 631 .
7 M. S. Starkey and P. E. Irving ( 1982 ) A comparison of the fatigue strength of machined and as‐cast surfaces of SG iron . Int. J. Fatigue 4 , 129 – 136 .

상세보기
8 B. A. Parker , D. S. Saunders and J. R. Griffiths ( 1982 ) A quantitative evaluation of microstructure of a strontium‐modified Al‐Si‐Mg alloy following prolonged solution treatment . Metals Forum 5 , 48 – 53 .
9 P. R. Austen and H. M. Williamson ( 1975 ) The effects of non‐standard ageing treatments on the fracture properties of Al‐Mg‐7wt%Si alloys . J. Aust. Inst. Metals 20 , 39 – 43 .
10 R. B. Heyward ( 1962 ) Designing Against Fatigue . Chapman & Hall , London .
11 D. M. Smith and J. A. Eady ( 1981 ) Properties of CP601—a widely used aluminium foundry alloy . Proc. 34th Conf., Australian Inst. Metals, Brisbane (available from Comalco Research Centre , Thomastown , Australia ).
12 M. Katcher and M. Kaplan ( 1974 ) Effects of R‐factor and crack‐closure on fatigue crack growth for aluminium and titanium alloys . ASTM STP 559 , pp. 264 – 282 .
13 W. Elber ( 1970 ) Fatigue crack closure under cyclic tension . Engng Fract. Mech. 2 , 37 – 45 .
14 A. J. McEvily ( 1977 ) Current aspects of fatigue . Metal Set. J. 11 , 274 – 284 .
15 H. U. Staal and J. D. Elen ( 1979 ) Crack closure and influence of cycle ratio R on fatigue crack growth in type 304 stainless steel at room temperature . Engng Fract. Mech. 11 , 275 – 283 .
16 V. Bachman and D. Munz ( 1979 ) Fatigue crack closure evaluation with the potential method . Engng Fract. Mech. 11 , 61 – 71 .
17 N. E. Dowling ( 1977 ) Crack growth during low‐cycle fatigue of smooth axial specimens . ASTM STP 637 , pp. 97 – 121 .
18 D. Wilhem , J. FitzGerald , J. Carter and D. Dittmer ( 1981 ) An empirical approach to determining K for surface cracks . Proc. 5th. Int. Conf. on Fracture , Cannes , Vol. 1 , pp. 11 – 21 .
19 C. C. Wigant and R. I. Stephens ( 1987 ) Fatigue crack growth behaviour of A356‐T6 cast aluminium alloy . Fatigue 87 1 , 165 – 173 .
20 R. W. Landgraf , J. D. Morrow and T. Endo ( 1969 ) Determination of the cyclic stress‐strain curve . J. Mater. 4 , 176 – 188 .
21 S. Suresh and R. O. Ritchie ( 1984 ) Propagation of short fatigue cracks . Int. Metals Rev. 29 , 445 – 476 .
22 A. Fathulla , B. Weiss and R. Stickler ( 1984 ) Int. Spring Meeting on Crack Initiation Under Complex Loading , Paris , p. 182 , organized by the French Commission of Metal Fatigue.

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관 관리번호, 논문명, 대등논문명, 저자 , 저널/프로시딩명, 발행기관, 발행년, 발행언어, 권, 호, 시작페이지, 끝페이지, ISBN, ISSN, 주제분야, 키워드, 초록(한글), 초록(영문), 저자(소속기관)
저장형식	Text(ASCII format) Excel format RefWorks Direct Export RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증

CASTING DEFECTS AND THE FATIGUE BEHAVIOUR OF AN ALUMINIUM CASTING ALLOY

Abstract ▼ AI-Helper

참고문헌 (22)

이 논문을 인용한 문헌

관련 콘텐츠

원문 URL 링크

이 논문과 함께 이용한 콘텐츠

AI-Helper ※ AI-Helper는 오픈소스 모델을 사용합니다.

선택된 텍스트