Recently we suffered lot of failures of polymer surge arresters made by same manufacture after one year field operation. In order to set up countermeasures we investigated the causes of failures. We extracted faulted arresters and sound ones which were installed in same pole with faulted ones for th...

Recently we suffered lot of failures of polymer surge arresters made by same manufacture after one year field operation. In order to set up countermeasures we investigated the causes of failures. We extracted faulted arresters and sound ones which were installed in same pole with faulted ones for the electrical test and dissection. 44 arresters were removed from 8 branch offices. Almost all of faulted arresters hadtracking damage on the interface between inner module and housing and the surface of inner module was very rough and irregular. It was possible to occur moisture ingress into the interface between inner module and housing due to the void of the interface and non tight sealing caps. Lots of sound arresters were failed during the moisture ingress test. This result must relate with tracking damage of faulted arresters. Therefore we can say that arresters had poor interface and sealing system. But we could not found aging and defects of ZnO elements because the electrical performance except moisture ingress test of arresters showed good.