The nano-sized Ce-doped YAG(Yttrium Aluminum Garnet, $Y_3Al_5O_{12}$) phosphor powders were prepared by combustion method from a mixed aqueous solution of metal nitrates, using citric acid as a fuel. The luminescence formation process and structure of phosphor powders were investigated by...

The nano-sized Ce-doped YAG(Yttrium Aluminum Garnet, $Y_3Al_5O_{12}$) phosphor powders were prepared by combustion method from a mixed aqueous solution of metal nitrates, using citric acid as a fuel. The luminescence formation process and structure of phosphor powders were investigated by means of XRD, SEM and PL. The XRD patterns show that YAG phase can form at all of the $Ce^{3+}$ concentration. However, when $Ce^{3+}$ concentration is over 2.0mol%, XRD patterns show $CeO_2$ peak between (321) peak and (400) peak. The pure crystalline YAG:Ce with uniform size of 30nm was obtained at 0.6mol% of the $Ce^{3+}$ concentration. The crystalline YAG:Ce powders showed broad emission peaks in the range 475~630nm and had maximum intensity at 526nm.