The effects of accelerated UV radiation on EPDM used for a polymeric insulator were investigated by contact angle, surface voltage decay after corona charging, SEM-EDX, ATR-FTIR and XPS. EPDM occurs as loss of hydrophobicity by UV treatment, which followed by surface cracking and chalking. The surfa...

The effects of accelerated UV radiation on EPDM used for a polymeric insulator were investigated by contact angle, surface voltage decay after corona charging, SEM-EDX, ATR-FTIR and XPS. EPDM occurs as loss of hydrophobicity by UV treatment, which followed by surface cracking and chalking. The surface voltage decay on UV-treated EPDM show that the shorter decay time corresponded to the treated samples with a longer UV exposure time. The surface oxygen and aluminum content were found to increase and carbon decrease, as is observed in EDX analysis. The ATR-FTIR and XPS indicated that C-C and C-H groups decreased and the highly oxidized carbon bonds such as C-O, C=O and O-C=O increase with time. Also, the effects of surface charges on hydrophobicity based on our results is discussed.