The Mar-M-247 alloy is one of the most widely used materials for gas turbine components in aerospace filed and it shows excellent high temperature strength properties. Hot section parts, such as turbine nozzle and blade, are difficult to manufacture because of their complicated shape. So, the joinin...

The Mar-M-247 alloy is one of the most widely used materials for gas turbine components in aerospace filed and it shows excellent high temperature strength properties. Hot section parts, such as turbine nozzle and blade, are difficult to manufacture because of their complicated shape. So, the joining process usually applies to them. In this study, the high-temperature behavior of Mar-M-247 alloy at liquid diffusion bonding was investigated. Thus, we performed the diffusion bonding at $1,121^{\circ}C$ for 7 minutes, and observed changes in high temperature strength. As a result, the strength of the bonded specimens decreased by about 70% at $649^{\circ}C$, 60% at $825^{\circ}C$, and 45% at $1,000^{\circ}C$ compared to the base metal. As a result of observing the strength change with bonding time, the specimen bonded for 720 minutes showed a similar strength with the base metal at $649^{\circ}C$. Inferring this result, the joint is considered to be the one-body part.