The new green $Al_3GdB_4O_{12}:Tb^{3+} and red Al_3GdB_4O_{12}:Eu_{3+}$ phosphors were synthesized and then characterized their optical properties for PDP application. And also the photoluminescence properties of these phosphors were compared with the commercial green $Zn_2SiO_4:Mn^{...

The new green $Al_3GdB_4O_{12}:Tb^{3+} and red Al_3GdB_4O_{12}:Eu_{3+}$ phosphors were synthesized and then characterized their optical properties for PDP application. And also the photoluminescence properties of these phosphors were compared with the commercial green $Zn_2SiO_4:Mn^{2+} and (Y,Gd)BO_3: Eu^{3+}$ red PDP phosphors. The phosphors were synthesized by solid state reaction at 115$0^{\circ}C$ for 4hr. It was found that the emitting brightness of $Al_3GdB_4O_{12}:Tb^{3+}$(15mol%) green phosphor under 147nm excitation was higher than that of commercial $Zn_2SiO_4: Mn^{2+}$ green PDP phosphor. However, the color coordinate of this new green phosphor was inferior to the commercial one. On the other hand, the emitting intensity of $Al_3GdB_4O_{12}:Eu^{3+}$(15mol%) red phosphor was smaller than the $commercial(Y,Gd)BO_3: Eu^{3+}$ red one, but the CIE coordinate was slightly improved. The excitation spectrum showed that $Al_3GdB_4O_{12}$ phosphors had a strong excitation band at $\lambda=160nm$ associated with the host absorption. And the photoluminance excitation (PLE) intensity in VUV range for $Al_3GdB_4O_{12}:Tb^{3+}$ green phosphor was higher than that of $Zn_2SiO_4: Mn^{2+}$, but the PLE intensity of $Al_3GdB_4O_{12}:Eu^{3+}$ red phosphor was smaller than $(Y,Gd)BO_3: Eu^{3+}$.