초록 ▼

The invention relates to a cellulose solution manufacturing method including: performing an ozonation treatment to bring a cellulose-containing material and ozone into contact with each other; and performing an alkali treatment to bring the obtained treated material and an alkali aqueous solution in

The invention relates to a cellulose solution manufacturing method including: performing an ozonation treatment to bring a cellulose-containing material and ozone into contact with each other; and performing an alkali treatment to bring the obtained treated material and an alkali aqueous solution into contact with each other, thereby dissolving at least cellulose in the cellulose-containing material brought into contact with the ozone in the alkali aqueous solution. According to the invention, it is possible to provide a method of manufacturing a cellulose solution in which cellulose can be dissolved in a more simple manner, a method of manufacturing a cellulose precipitate in which cellulose can be recovered from the cellulose solution, and a method of saccharifying cellulose which uses the cellulose precipitate.

대표청구항 ▼

1. A cellulose solution manufacturing method comprising: providing a cellulose-containing material, wherein said cellulose-containing material comprises at least one of cotton, lyocell, rayon, and cupra;contacting said cellulose-containing material with ozone to obtain an ozonated cellulose-containi

1. A cellulose solution manufacturing method comprising: providing a cellulose-containing material, wherein said cellulose-containing material comprises at least one of cotton, lyocell, rayon, and cupra;contacting said cellulose-containing material with ozone to obtain an ozonated cellulose-containing material;drying said ozonated cellulose-containing material at a temperature in the range of 50° C. to 160° C. to obtain a dried treated material;mixing said dried treated material with a 1N to 5N sodium hydroxide aqueous solution to obtain a mixture; andmaintaining said mixture at a temperature of −10° C. to 50° C. for 0.1 minute to 60 minutes to dissolve at least cellulose and obtain a cellulose solution comprising dissolved cellulose having a polymerization degree of 50 to 50,000. 2. The method of claim 1, wherein said ozone is present at a concentration of 1 mg/L to 300 mg/L, and a time of contacting said cellulose-containing material with said ozone is 1 minute to 300 minutes. 3. The method of claim 1, further comprising: adjusting a pH of said cellulose solution to pH 7 or less to precipitate and obtain a cellulose precipitate. 4. The method of claim 1, further comprising: extruding said cellulose solution into an acid aqueous solution to obtain a cellulose precipitate. 5. The method of 4, wherein said acid aqueous solution has a pH from 1.0 to 6.9 and a concentration of acid from 1 wt % to 50 wt %. 6. The method of claim 3, further comprising: saccharifying said cellulose precipitate in the presence of a cellulolytic enzyme to thereby obtain an aqueous solution containing water-soluble oligosaccharides or glucose. 7. The method of claim 1, wherein said dissolved cellulose in said cellulose solution is capable of forming a cellulose precipitate having a cellulose content of 50 wt % to 100 wt %. 8. The method of claim 1, wherein said temperature of said mixture is maintained at −5° C. to 30° C. for 1 minute to 30 minutes. 9. A cellulose solution manufacturing method comprising: providing a cellulose-containing material, wherein said cellulose-containing material comprises at least one of cotton, lyocell, rayon, and cupra;contacting said cellulose-containing material with ozone to obtain an ozonated cellulose-containing material;drying said ozonated cellulose-containing material at a temperature in the range of 50° C. to 160° C. to obtain a dried treated material;mixing said dried treated material with an aqueous solution consisting of 1N to 5N sodium hydroxide and water to obtain a mixture; andmaintaining said mixture at a temperature of −10° C. to 50° C. for 0.1 minute to 60 minutes to dissolve at least cellulose and obtain a cellulose solution comprising dissolved cellulose having a polymerization degree of 50 to 50,000.