초록

대기중에서 유도용해한 여러조성의 Cu-Zn-Al 및 Cu-Al-Ni 합금에 미량 합금 원소 인 Ni, B, Ti, Zr, Si 등을 적당히 첨가하고 소정의 열처리를 시행하여 합금조성및 미량 합금원소가 기계적 성질및 상변태에 미치는 영향을 규명한 후 최적 합금조성을 확립한다. 이러한 합금설계와 여러 가지 형상기억 성능실험도 병행하고자 한다. 또한 개발된 합금의 기계적 성질과 상변태에 관한 연구도 수행한다. 그리고 microstructure는 광학현미경과 X-ray, SEM(주사전자현미경), TEM(투과전자현미경)으로 분석한다

Abstract ▼

A new Cu-Zn-Al shape memory alloy has been developed by the addition of microalloying elements (Zr, Ti, Ni and Si) to Cu-Zn-Al base. The composition was Cu -24.5Zn -4Al -1Ni -0.2Si -0.18Zr -0.19Ti. The developed alloy exhibited good tensile properties compared to other Cu-base shape memory alloy. Th

A new Cu-Zn-Al shape memory alloy has been developed by the addition of microalloying elements (Zr, Ti, Ni and Si) to Cu-Zn-Al base. The composition was Cu -24.5Zn -4Al -1Ni -0.2Si -0.18Zr -0.19Ti. The developed alloy exhibited good tensile properties compared to other Cu-base shape memory alloy. The enhancement was due to the refinement of grain and martensite variant. The tensile strength (56 kg/$mm^2$ = 550 MPa) and the elongation (10-11%) of the developed alloy were 2-3 times larger than those of coarse grained Cu-Zn-Al alloys. In addition, the developed alloys showed an excellent shape memory recovery(above 90%), and exhibited a good thermal stabilization at temperatures below $l00^{\circ}C$. The $M_s$ temperature of the alloy was $36^{\circ}C$. Therefore, this alloy may be used at temperatures below $l00^{\circ}C$ and replace the Ni-Ti alloy in various application fields.
For the further improvement of the tensile strength, new Cu-Al-Ni shape memory alloys have been developed by the addition of microalloying elements (Zr). The chemical compositions were Cu -13.5Al -3Ni -0.54Zr and Cu -12.8Al -4Ni - 0.32Zr. The developed alloys showed excellent tensile strength (83 kg/$mm^2$ = 810 MPa) compared to developed Cu-Zn-Al shape memory alloy. They also exhibited an excellent shape memory recovery (above 85 %) at a 3 percent strain.
In next research, various properties will be investigated in developed Cu-Al-Ni shape memory alloys.

목차 Contents

• 제1장 서 론...9
• 제2장 실험절차...10
• 제1절 합금조성의 선택...10
• 제2절 열처리 및 제조공정...10
• 제3절 시편제작...13
• 제4절 기계적 성질 실험...13
• 제5절 변태온도 및 상변태 실험...16
• 제6절 미세조직 및 상변화 관찰...16
• 제3장 실험결과 및 고찰...17
• 제1절 인장성질...17
• 제2절 형상기억 성능 및 형상기억효과의 원인...28
• 제3절 변태온도...31
• 제4절 미세조직...35
• 제5절 항온 열처리...38
• 제4장 결 론...55
• 제5장 참고문헌...57