초록

연구개발의 내용 및 범위
극저온 시험장치의 특성을 평가하여개선해야 될 부분을 많이 보완하였으며 극저온 시험에 필요한 각종 특수 측정장치를 구매 확보하였다. 극저온 시험.평가기술에 대한 연구동향을 파악하였고 극저온 시험과 관련된 문제점을 검토하였다. 1차년도에서 우선적으로 액체질소온도에서의 실험을 수행하였으며 실험결과는 만족할 만한 것으로 나타났다.

Abstract ▼

The low temperature testing facility has been improved in many ways through evaluation of its characteristics and several special equipments for low temperature testing were purchased. Tendency in the low temperature research was discussed including problems in standardization of low temperature tes

The low temperature testing facility has been improved in many ways through evaluation of its characteristics and several special equipments for low temperature testing were purchased. Tendency in the low temperature research was discussed including problems in standardization of low temperature testing.
On the 1st year of research, tests at liquid nitrogen temperature were carried out and the experimental results were satisfactory.

목차 Contents

• 제1장 연구 사업의 개요...12
• 제1절 서설...12
• 제2절 연구 개발의 배경과 필요성...15
• 제3절 연구 개발의 목표...18
• 제4절 연구의 내용 및 범위...19
• 제5절 기술 연수 및 전문가 활용...19
• 제2장 극저온 재료의 개발 동향...22
• 제1절 서설...22
• 제2절 국내외의 개발 동향...23
• 1. 국외의 개발 동향...23
• 2. 국내의 개발 동향...28
• 제3절 극저온에서의 시험 방법 표준화...30
• 제3장 구조용 저온 재료...38
• 제1절 서설...38
• 제2절 오스테나이트계 스텐레스강...41
• 1. 소둔된 상태의 300계열 스텐레스강...45
• 2. 소둔된 질소 강화형 스텐레스강...51
• 3. 냉간 가공된 Sheet 형태의 300계열 스텐레스강...53
• 제3절 니켈강...53
• 1. 니켈강의 분류...53
• 2. 니켈강의 열처리...56
• 3. 니켈강의 기계적 성질...57
• 제4절 알루미늄 합금...64
• 제4장 오스테나이트계 스텐레스강의 극저온 특성...68
• 제1절 서설...68
• 제2절 변형 속도의 영향...69
• 제3절 제어 방식의 영향...77
• 제5장 극저온 시험 장치...80
• 제1절 서설...80
• 제2절 극저온 시험 장치의 원리 및 구조...81
• 제3절 극저온 시험 장치...85
• 제6장 극저온에서의 기계적 시험...99
• 제1절 서설...99
• 제2절 인장 시험...100
• 1. 시험 방법...100
• 2. 시험 결과...104
• 제3절 파단면 관찰...113
• 제7장 앞으로의 연구 방향...118
• 제8장 연구 결과 및 결과 활용에 대한 건의...122
• 제1절 연구 결과...122
• 제2절 연구 결과 활용 방안에 대한 건의...123
• 참고문헌...125