$Na_2O-CaO-MgO-Al_2O_3-SiO_2$ glass was taken as a basic glass and then $Li_2O$ O.5wt%, $K_2O$ 2.0wt% were substituted to $Na_2O$content, MgO 12.0wt %, ZnO 6.0wt % to CaO content. And also nucleation agent $ZrO_2 and $CaF_2$ were adde...

$Na_2O-CaO-MgO-Al_2O_3-SiO_2$ glass was taken as a basic glass and then $Li_2O$ O.5wt%, $K_2O$ 2.0wt% were substituted to $Na_2O$content, MgO 12.0wt %, ZnO 6.0wt % to CaO content. And also nucleation agent $ZrO_2 and $CaF_2$ were added to 1-2wt% respectively. The crystal according to the compositions appeared wollastonite, diopside and diopside.tremolite. The glasses substituted NazO by LizO was decreased thermal expansion coeffcient but substituted by ZnO was opposite direction and both of them increased bending strength. In the ratio of ZrOz to CaF, each 1: 1 and 1: 2 have shown considerable crystal growth at $1000^{circ}C~1050^{\circ}C$ and high bending strength, but the glass in the ratio 1: 2 have shown lowest thermal expansion coefficient. The activation energy was at the glass in the ratio of ZrO, to CaFz 1:2 evaluated 55.24kvsl/mol by Ozawa type and 53.05kal/mol by kissinger type.