The effect of stuffing of TiN on the diffusion barrier property between A1 and Si was investigated. The stuffing of TiN was performed by annealing in a Nz ambient at $450^{\circ}C$ for 30min. By TEM analysis, it is identified that there are solid-free or open spaces of a b u t 10-20$...

The effect of stuffing of TiN on the diffusion barrier property between A1 and Si was investigated. The stuffing of TiN was performed by annealing in a Nz ambient at $450^{\circ}C$ for 30min. By TEM analysis, it is identified that there are solid-free or open spaces of a b u t 10-20$\AA$ between the grains of asdeposited TiN. In the case of stuffed TiN, the width of solid-free or open spaces has been reduced to about 10$\AA$ or below. The combination of RBS and AES analyses showed that the asdeposited TiN had about 7at.% of oxygen, and that the stuffed TiN had about 10-15at.% of oxygen. The diffusion barrier test result shows that after annealing at $650^{\circ}C$ for lhour, the asdeposited TiN fails due to the formation of A1 spikes and Si pits in the Si substrate. However, in the case of stuffed TiN, there is no indication of Al spikes and Si pits at the same annealing condition. Thus, it is concluded that this stuffing of TiN significantly improves the diffusion barrier property of TiN between A1 and Si. It is considered that the stuffing effect results from the reduced diffusion through grain boundaries due to the reduced spacing of grain boundaries.