The microstructural and textural development during rolling is compared in two Hadifield's steels (high Mn steel), one having low carbon content (0.65 wt.%) and the other high carbon (1.35 wt.%).In low carbon Hadfield's steel (LCHS) mixed microstructures are formed which contain intrinsic stacking f...

The microstructural and textural development during rolling is compared in two Hadifield's steels (high Mn steel), one having low carbon content (0.65 wt.%) and the other high carbon (1.35 wt.%).In low carbon Hadfield's steel (LCHS) mixed microstructures are formed which contain intrinsic stacking faults, deformation twins, and brass type shear bands. The deformation twins are thought to be formed by the stacking of intrinsic stacking faults. The similar development to 70-30 brass texture is observed in early deformation. However the abnormal texture is developed after 40 % deformation, which is thought to be due to the martensite phase transformation. In high carbon Hadfield's steel (HCHS) mixed substructures of dislocation tangles, deformation twins, and shear bands (both copper and brass type) are found to develop. The texture development is similar to that of 70-30 brass. This is consistant with no carbon segregation and no martensitic phase transformation in HCHS. In spite of the difference of substructure and texture development during rolling in two steels, the difference in stacking fault energy is measured to be small ($2 mJm^-2$). The carbon segregation is only occurred in LCHS. Thus it is thought that the carbon segregation influence the microstructure and texture development during rolling. This is related with martensite phase transformation in LCHS.

주제어