Polyurethane (PU) synthesized from 4,4'-diphenylmethane diisocyanate having high functionality (f=2.9) and polyester polyol have been investigated by differential scanning calorimeter (DSC), dynamic mechanical thermal analyzer (DMTA), and Fourier transform infrared spectroscope (FT-IR). From the DSC...

Polyurethane (PU) synthesized from 4,4'-diphenylmethane diisocyanate having high functionality (f=2.9) and polyester polyol have been investigated by differential scanning calorimeter (DSC), dynamic mechanical thermal analyzer (DMTA), and Fourier transform infrared spectroscope (FT-IR). From the DSC measurement of polyurethane, a single transition temperature ($T_g$) was observed. This result indicates that polyurethanes synthesized in this work have homogeneous network structure due to high functionality of diisocyanate. It was also found that the $T_g$ of polyurethane was increased as hard segment content was increased. The results from DMTA measurement are consistent with DSC results. In order to investigate the effect of thermal annealing on the $T_g$ of polyurethane, the samples were annealed at various annealing conditions. $T_gs$ of polyurethanes were found to increased with annealing temperature. From swelling experiment and FT-IR studies, it was found that the $T_g$ was increased as crosslinking density of polyurethane was increased.

주제어