Elelctrical properties of $BaTiO_3$ were characterized with addition of $Y_2O_3, CaO,SiO_2$ and Mn to develope the composition of PTC thermistor suitable as a current limiting device for automobile motor system. With the addition of 0.2 mol% $Y_{2}O_3$ to $BaTiO...

Elelctrical properties of $BaTiO_3$ were characterized with addition of $Y_2O_3, CaO,SiO_2$ and Mn to develope the composition of PTC thermistor suitable as a current limiting device for automobile motor system. With the addition of 0.2 mol% $Y_{2}O_3$ to $BaTiO_3$, the minimum resistance of 16.5 ${\Omega}{\cdot}$cm was obtained at room temperature. $(Ba_{0.996}Y_{0.004})TiO_3$ exibited a minimum resistance of 50${\Omega}{\cdot}$cm with addition of 1.6 mol% $SiO_2$. The grain size of $(Ba_{0.996}Y_{0.004})TiO_3$ decreased from 34.95 ${\mu}$m to 13.4 ${\mu}$m and thus breakdown voltage could be improved by changing the composition as $(Ba_{0.996}Y_{0.004}Ca_{0.05}) TiO_3$ with substition of 5 mol% Ca into Basites. When 0.04 mol% Mn was added, the optimum PTCR properties could be obtained : the resistivity at room temperature and ${\rho}_{max}/{\rho}_{min}$ were 30~40${\Omega}{\cdot}$cm and $1.5{\times}10^5$ respectively.