This study was performend to examine Poisson's ration of polymer-modified asphalt concrete due to temperature variatino . Asphalt binder used in this study was an AC85-100, penetration grade of 85-100, and polymer for modifying asphalt were domestic LDPE(Low-density polyethylene) and SBS(Styrene-but...

This study was performend to examine Poisson's ration of polymer-modified asphalt concrete due to temperature variatino . Asphalt binder used in this study was an AC85-100, penetration grade of 85-100, and polymer for modifying asphalt were domestic LDPE(Low-density polyethylene) and SBS(Styrene-butadiene-styrene). Aggregate was a crushed gneiss which was most widely used in the middle part of Korea. Using these materias, asphalt mixture slab(340mm$\times$240mm$\times$80mm) with optimum asphalt content from mix design was made and cut into square pillar (80mm$\times$80mm$\times$160mm). Poisson's ration was measured in various temperture (-15$^{\circ}C$, -1$0^{\circ}C$, -5$^{\circ}C$,$0^{\circ}C$,5$^{\circ}C$,1$0^{\circ}C$ and 2$0^{\circ}C$) under the load of one axis repeated compression mode. Poisson's ration of normal asphalt polymer modified asphalt mixtures in normal temperatures. This indicated that AP mixture was more susceptible to temperature effects. From regression aalysis of experimental results, the difference of Poisson's ration between normal and low temperature showed that polymer modified asphalt mixture were lower than AP mixture except for SBS modified asplat mixture.

Keyword