Synthesize of anatase type $TiO_2$ from $TiCl_4$ solution was studied. KOH was used on dehydration reaction of $TiCl_4$ solution. Products of dehydration reaction was calcined at 300, 500, 700, 900, $1000^{\circ}C$ during 1hour. Calcined products was studi...

Synthesize of anatase type $TiO_2$ from $TiCl_4$ solution was studied. KOH was used on dehydration reaction of $TiCl_4$ solution. Products of dehydration reaction was calcined at 300, 500, 700, 900, $1000^{\circ}C$ during 1hour. Calcined products was studied by XRD, DTA, and FT-IR for effect of calcined temperature. The results are as follow. \circled1 Product pf dehydration reaction at$ 90^{\circ}C$ was semicrystalline anatase type $TiO_2$ because it has a peak vary broad and low at the position of anatase crysral XRD pattern. \circled2 Pure titanium oxide semi-crystalline products were produced at acid pH condition which convert to anatase crystal at $300^{\circ}C$ and to rutile crystal at $700^{\circ}C$. \circled3 The chemical composition of semicrystalline products which was produce at alkali pH conditions, were potasium titante. Potasium-titanate semi-crystalline products crystallized at 630~$640^{\circ}C$ \circled4 The transition temperature of potassium dopped titanium oxide semi-crystalline products was increased with the contents of potasium. \circled5 The optimum synthesise condition of anatase $TiO_2$ products from $TiCl_4$ and KOH are pH 3~5 and $300^{\circ}C$ calcination.