In the flip chip interconnection using solder bump, the Under Bump Metallurgy (UBM) is required to perform multiple functions in its conversion of an aluminum bond pad to a solderable surface. In this study, various UBM systems such as $Al 1\mu\textrm{m} / Ti 0.2\mu\textrm{m} / Cu 5\mu\textrm{m...

In the flip chip interconnection using solder bump, the Under Bump Metallurgy (UBM) is required to perform multiple functions in its conversion of an aluminum bond pad to a solderable surface. In this study, various UBM systems such as $Al 1\mu\textrm{m} / Ti 0.2\mu\textrm{m} / Cu 5\mu\textrm{m}, Al 1\mu\textrm{m} / Ti 0.2\mu\textrm{m} / Cu 1\mu\textrm{m}, al 1\mu\textrm{m}/Ni 0.2\mu\textrm{m} / Cu 1\mu\textrm{m} and Al 1\mu\textrm{m}/Pd 0.2\mu\textrm{m} / Cu 1\mu\textrm{m}$ for flip chip interconnection using the low melting point eutectic 63Sn-37Pb solder were investigated and compared to their metallurgical properties. $100\mu\textrm{m}$ size bumps were prepared for using an electroplating process. The effects of the number of reflows and aging time on the growth of intermetallic compounds(IMC) were investigated. $Cu_6Sn_5$ and $Cu_3Sn$ IMC were abserved after aging treatment in the UBM system with thick coper $(Al 1\mu\textrm{m}/Ti 0.2\mu\textrm{m}/Cu 5\mu\textrm{m})$. However only the $Cu_6Sn_5$ was detected in the UBM system with $1\mu\textrm{m}$ thick copper even after 2 reflow and 7 day aging at $150^{\circ}C$. Complete Cu consumption by Cu-Sn IMC growth gives rise to a direct contact between solder inner layer such as Ti, Ni and Pd, and hence to possibly cause reactions between two of them. In this study, however, only for the Pd case, IMC of PdSn. was observed by Cu consumption. UBM interfacial reactions with s이der affected the adhesion strength ot s이der balls after s이der reflow and annealing treatment.