초록

용어보기논문에서 용어와 풀이말을 자동 추출한 결과로, 시범 서비스 중입니다. AI-Helper

Abstract ▼ AI-Helper

Cerium substituted YIG thin films were grown by rf magnetron sputter techniques. We investigated the effects of post-deposition heat-treatment as well as various deposition parameters such as substrate materials, substrate temperature. sputter power, and sputter gas types on the crystallinity, chemi...

Cerium substituted YIG thin films were grown by rf magnetron sputter techniques. We investigated the effects of post-deposition heat-treatment as well as various deposition parameters such as substrate materials, substrate temperature. sputter power, and sputter gas types on the crystallinity, chemical composition, microstructure and magnetic characteristics of the films. Post-deposition heat treatment over 750 $\^{C}$ was applied to crystallize as-prepared amorphous films, and a strong tendency of particular crystallographic planes tying parallel to substrate surface was observed for the post-deposition heat-treated films on GGG substrate. The chemical composition of the films exhibited a wide range of chemical stoichiometry depending on the oxygen fraction of sputter gas, and in particular the composition of the film deposited in sputter gas with an oxygen fraction of R = 10% was Ce$\_$0.23/Y$\_$1.30/Fe$\_$3.50/O$\_$12/. With raising the temperature of post-deposition heat-treatment from 900 $\^{C}$ to 1100 $\^{C}$, the surface roughness of the film on GGG substrates increased from about 3 nm to 40 nm, but their coercive force and ferromagnetic resonance line width decreased from 0.477 kA/m to 0.369 kA/m and from 12.5 kA/m to 8.36 kA/m, respectively.