It is difficult to meet the cleanliness requirement of $10^{10}/\textrm{cm}^2$ for the giga level device fabrication with mechanical cleaning techniques like scrubbing which is widely used to remove the particles generated during Chemical Mechanical Polishing (CMP) processes. Therefore, t...

It is difficult to meet the cleanliness requirement of $10^{10}/\textrm{cm}^2$ for the giga level device fabrication with mechanical cleaning techniques like scrubbing which is widely used to remove the particles generated during Chemical Mechanical Polishing (CMP) processes. Therefore, the second cleaning process is needed to remove metallic contaminants which were not completely removed during the mechanical cleaning process. In this paper the experimental results for the removal of the metallic contaminants existing on the wafer surface using remote plasma $H_2$ cleaning and UV/$O_3$ cleaning techniques are reported. In the remote plasma $H_2$ cleaning the efficiency of contaminants removal increases with decreasing the plasma exposure time and increasing the rf-power. Also the optimum process conditions for the removal of K, Fe and Cu impurities which are easily found on the wafer surface after CMP processes are the plasma exposure time of 1min and the rf-power of 100 W. The surface roughness decreased by 30-50 % after remote plasma $H_2$ cleaning. On the other hand, the highest efficiency of K, Fe and Cu impurities removal was achieved for the UV exposure time of 30 sec. The removal mechanism of the metallic contaminants like K, Fe and Cu in the remote plasma $H_2$ and the UV/$O_3$ cleaning processes is as follows: the metal atoms are lifted off by $SiO^*$ when the $SiO^*$is evaporated after the chemical $SiO_2$ formed under the metal atoms reacts with $H^+ \; and\; e^-$ to form $SiO^*$.