Tin plating on component finishes may grow whiskers under certain conditions, which may cause failures in electronics equipment. To protect the environment, 'lead-free' among component finishes is being promoted worldwide. This paper presents the evaluation results of whiskers on two kinds of lead-f...

Tin plating on component finishes may grow whiskers under certain conditions, which may cause failures in electronics equipment. To protect the environment, 'lead-free' among component finishes is being promoted worldwide. This paper presents the evaluation results of whiskers on two kinds of lead-free plating materials at the plating temperature and under the reliability test. The rising plating temperature caused increasing the size of plating grain and shorting the growth of whisker. The whisker was grown under the temperature cycling the bent type in matt Sn plating and striated type in malt Sn-Bi. The whisker growth in Sn-Bi plating was shorter than that in Sn plating. In FeNi42 leadframe, the $7.0{\~}10.0{\mu}m$ diameter and the $25.0{\~}45.0{\mu}m$ long whisker was grown under 300 cycles. In the 300 cycles of Cu leadframe, only the nodule(nuclear state) grew on the surface, and in the 600 cycles, a $3.0{\~}4.0{\mu}m$ short whisker grew. After 600 cycles, the ${\~}0.34{\mu}m$ thin $Ni_3Sn_4$ formed on the Sn-plated FeNi42. However, we observed the amount of $0.76{\~}1.14{\mu}m$ thick $Cu_6Sn_5$ and ${\~}0.27{\mu}m$ thin $Cu_3Sn$ intermetallics were observed between the Sn and Cu interfaces. Therefore, the main growth factor of a whisker is the intermetallic compound in the Cu leadframe, and the coefficient of thermal expansion mismatch in FeNi42.

주제어