Nowadays, recycling of aggregates from the waste concrete is in big demand due to the protection of environment and the shortage of aggregates that are needed for ever expanding construction projects. This study was undertaken to examine the feasibility of recycling waste concrete powder produced in...
Nowadays, recycling of aggregates from the waste concrete is in big demand due to the protection of environment and the shortage of aggregates that are needed for ever expanding construction projects. This study was undertaken to examine the feasibility of recycling waste concrete powder produced in the crushing process of demolished concrete as a filler material for polymer mortar. In this study, polymer mortar specimens were prepared by varying the mix proportion of polymer binder (ranging 9~15 wt%), waste concrete powder (ranging 0~20 wt%) substituted for silica powder, 0.1~0.3 mm fine aggregate (ranging 21~24 wt%) and 0.7~1.2 mm fine aggregate (ranging 44~47 wt%). For the prepared polymer mortar specimens, various physical properties such as strength, water absorption, heat water resistance, acid resistance, pore distribution and SEM observation were investigated in this work. As a result, physical properties of polymer mortar were observed to have remarkably improved with an increase of polymer binder, but greatly deteriorated with an increase of substitution quantity of waste concrete powder.
Nowadays, recycling of aggregates from the waste concrete is in big demand due to the protection of environment and the shortage of aggregates that are needed for ever expanding construction projects. This study was undertaken to examine the feasibility of recycling waste concrete powder produced in the crushing process of demolished concrete as a filler material for polymer mortar. In this study, polymer mortar specimens were prepared by varying the mix proportion of polymer binder (ranging 9~15 wt%), waste concrete powder (ranging 0~20 wt%) substituted for silica powder, 0.1~0.3 mm fine aggregate (ranging 21~24 wt%) and 0.7~1.2 mm fine aggregate (ranging 44~47 wt%). For the prepared polymer mortar specimens, various physical properties such as strength, water absorption, heat water resistance, acid resistance, pore distribution and SEM observation were investigated in this work. As a result, physical properties of polymer mortar were observed to have remarkably improved with an increase of polymer binder, but greatly deteriorated with an increase of substitution quantity of waste concrete powder.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.