알루미늄의 브레이징과 원리
Aluminum Brazing and Its Principle 원문보기

마이크로전자 및 패키징 학회지 = Journal of the Microelectronics and Packaging Society, v.24 no.4, 2017년, pp.1 - 7

이순재 (서울시립대학교 신소재공학과) , 정도현 (서울시립대학교 신소재공학과) , 정재필 (서울시립대학교 신소재공학과)

Abstract ▼ AI-Helper

Aluminum alloys have been widely used in many fields such as electronic, structure, aero-space and vehicle industries due to their outstanding thermal and electrical conductivity as well as low cost. However, they have some difficulties for using in brazing process because of the strong oxide layer of $Al_2O_3$ on the surface of Al alloy. In addition, their melting point is similar to that of brazing filler metal resulting in thermal damage of Al alloys. Therefore, it is very important to understand the brazing principles, filler metal and its properties such as wetting, capillary flow and dissolution of base metal in the Al brazing process. This paper reviews the brazing principles, aluminum alloys, and brazing fillers. In the case of brazing principle, some formula was used for calculation of capillary force and the dissolution to obtain the best condition of Al brazing. In addition, the advanced research trends in Al brazing were introduced including thermal treatment, additive for improving property and decreasing melting point in Al brazing process.

주제어

AI 본문요약
AI-Helper

문제 정의

본고는 알루미늄 브레이징의 원리, 젖음성 및 모세관현상과 모재의 용해 현상을 최근 연구동향과 함께 소개하였다. 또한 알루미늄의 종류와 특성, 브레이징 합금에 대하여도 서술하였다.

성능/효과

알루미늄은 열 및 전기전도도가 우수하고, 경량금속이며 내식성 및 강도도 우수하여 전자 산업을 포함한 산업 전반에 열교환기와 경량화 구조체로서 필수적인 금속이다. 알루미늄은 낮은 융점과 강한 산화막으로 인해 브레이징이 까다로운 점은 있지만, 브레이징 용가재 합금, 브레이징 공정 등 기술개발이 꾸준히 진행되고 있다. 이를 통하여 전자 및 패키징 산업, 이와 관련된 장비산업 등에서 보다 용이하게 알루미늄 합금을 사용할 수 있을 것으로 기대된다.

후속연구

알루미늄은 낮은 융점과 강한 산화막으로 인해 브레이징이 까다로운 점은 있지만, 브레이징 용가재 합금, 브레이징 공정 등 기술개발이 꾸준히 진행되고 있다. 이를 통하여 전자 및 패키징 산업, 이와 관련된 장비산업 등에서 보다 용이하게 알루미늄 합금을 사용할 수 있을 것으로 기대된다.

질의응답

핵심어	질문	논문에서 추출한 답변
	알루미늄의 활용분야는?	알루미늄은 철강재료에 비해 가볍고 전, 연성이 뛰어나며 표면에 산화막이 형성되어 내식성이 우수하다. 또한 전기 전도도와 열전도도가 우수하여 전기나 전자재료, 건축소재, 우주항공재료 등 다양한 분야에서 사용하고 있다.1-5) 전자산업에서는 회로나 제품 혹은 생산설비의 열교환기 등에서, 자동차산업에서는 차체 경량화 소재로 알루미늄의 사용이 증가하는 추세이다.
	알루미늄의 특징은?	알루미늄은 철강재료에 비해 가볍고 전, 연성이 뛰어나며 표면에 산화막이 형성되어 내식성이 우수하다. 또한 전기 전도도와 열전도도가 우수하여 전기나 전자재료, 건축소재, 우주항공재료 등 다양한 분야에서 사용하고 있다.
	알루미늄 소재를 접합하는 브레이징법이란?	알루미늄은 알루미늄 동종끼리의 접합 이외에도, 알루미늄과 이종금속 간의 접합에 관한 연구도 증가하고 있다.2,3) 알루미늄 소재를 접합하는 방법 중 브레이징법은 모재 사이에 용가재를 삽입하여, 모재는 용융시키지 않고 용가재만 용융시켜 접합하는 방법이다. 브레이징은 면접합법으로 한번에 여러 곳을 동시에 접합하여 생산성이 높고, 접합강도도모재 파단수준으로 강하며, 이종재료도 용이하게 접합할 수 있는 장점이 있다.

참고문헌 (47)

A. Sharma, and J. P. Jung, "Aluminium Based Brazing Fillers for High Temperature Electronic Packaging Applications", J. Microelectron. Packag. Soc., 22(4), 1 (2015).
A. Mathieu, S. Pontevicci, J. Viala, E. Cicala, S. Mattei, and D. Grevey, "Laser brazing of a steel/aluminium assembly with hot filler wire (88%Al, 12%Si)", Materials science & engineering: A, 435-436, 19 (2006).

상세보기
J. H. Lee, T. J. Yoon, K. H. Lee, S. Y. Kwak, and C. Y. Kang, "Microstructure and mechanical property of joint of Al-Steel laser brazing using Cu filler metal", The Korean Welding & Joining Society., 174 (2016).
R. J. Klein, "Soldering in electronics", 2nd Ed., (1989).
R. W. Messler. Jr, "Joining of advanced materials", Butterworth - Heinemann, 3-16 (1993).
P. T. Viance, "Soldering handbook", American Welding Society, 3rd Ed., (1999).
J. E. Hatch, "Aluminum:properties and physical metallurgy", American society for metals, 1 (1999).
X. Song, H. Li, and X. Zeng, "Brazing of C/C composites to Ti6Al4V using multiwall carbon nanotubes reinforced TiCuZrNi brazing alloy", J. Alloys and Compounds, 664, 175 (2016).

상세보기
X. Song, H. Li, X. Zeng, and L. Zhang, "Brazing of C/C composites to Ti6Al4V using grapheme nanoplates reinforced TiCuZrNi brazing alloy", Materials Letters, 183, 232 (2016).

상세보기
Z. Wang, G. Wang, M. Li, J. Lin, Q. Ma, A. Zhang, Z. Zhong, J. Qi, and J. Feng, "Three-dimensional graphene-reinforced cu foam interlayer for brazing C/C composites and Nb", Carbon, 118, 723 (2017).

상세보기
C. S. Kang, and J. P. Jung, "Micro joining", Samsung-Books, pp.22-23 (2002).
M. H. Sloboda, "Design and Strength of Brazed Joints", Johnson Matthey & Co limited, London, pp.3-6 (1961).
A. Shen, Y. Liu, X. Qiu, Y. Lu, and S. Liang, "A model for capillary rise in nano-channels with inherent surface roughness", Appl. Phys. Lett., 110, 121601 (2017).

상세보기
E. W. Washburn, "The dynamics of capillary flow", Phys. Rev., 17(3), 273 (1921).

상세보기
N. Fries, and M. Dreyer, "The transition from inertial to viscous flow in capillary rise", J. Colloid Interface Sci., 327, 125 (2008).

상세보기
H. Zhao, S. Elbel, and P. S. Hrnjak, "Capillary Flow of Liquid Metal Occurring in Microchannel Heat Exchanger Fabrication", (2012).
A. C. Hall, F. M. Hosking, and M. Reece, "Visual observations of liquid filler metal flow within braze gap", Science and Technology of Welding and Joining, 9(2), 95 (2002).
S. Chen, L. Li, Y. Chen, and J. Huang, "Joing mechanism of Ti/Al dissimilar alloys during laser welding-brazing process", Journal of Alloys and Compounds, 509, 891 (2011).

상세보기
D. Gupta, K. Vieregge, and W. Gust, "Interface diffusion in eutectic Pb-Sb solder", Acta Materilalia, 47, 5 (1998).

상세보기
H. T. Lee, and M. H. Chen, "Influence of intermetallic compounds on the adhesive strength of solder joints", Materials Science and Engineering: A, 333, 24 (2002).

상세보기
C. Hunt, and D. D. Maio, "A test methodology for copper dissolution in lead-free alloys", IPC APEX EXPO, (2009).
K. Barmak, "Dissolution kinetics of nickel in lead-free Sn0Bi-In-Zn-Sb soldering alloys", Proc. Mater. Re. Soc, Symp., 993, 0993-E03-01 (2007).
H. Nakagawa, C. H. Lee, and T. H. North, "Modeling of base metal dissolution behavior during transient liquid phase brazing", Metallurgical transaction A, 22(2), 543 (1991).

상세보기
D. U. Kim, C. Y. Kang, and W. J. Lee, "The effect of grain boundary on the dissolution of base metal into insert metal during TLP bonding of Ni-Base super alloy", Metals and Materials, 5(5), 377 (1999).
Y. Li, W. Liu, P. He, J. Feng, and D. P. Sekulic, "Dissolution of TiAl alloy during high temperature brazing", Journal of Materials Science, 48(15), 5247 (2013).

상세보기
K. Elangovana, and V. Balasubramanianb, "Influences of post-weld heat treatment on tensile properties of friction stirwelded aa6061 aluminum alloy joints", Material Characterization, 59, 1168 (2008).

상세보기
M. Craig, and G. Jin, "Aluminum brazing -what matter most: fundamentals and case studies", Ipsen Incorporated, Cherry Valley, Illionis USA (2017).
D. M. Jacobson, and H. Giles, "Principles of Brazing II", ASM international, 3rd Ed., pp.1-14 (2005).
S. Z. Lu, and A. Hellawell, "The mechanism of silicon modification in aluminum-silicon alloys:impurity induced twinning", Metallurgical transactions A, 18, 1721 (1987).

상세보기
M. M. Makhlouf, and H. V. Guthy, "The aluminum silicon eutectic reaction: mechanisms and crystallography.", Journal of light metals, 1, 199 (2001).

상세보기
D. J. Fray, "Determination of sodium in molten aluminum and aluminum alloys using beta alumina probe", Metallurgical transactions B, 8(1), 153 (1977).

상세보기
A. Knuutinen, K. Nogita, S. D. McDonald, and A. K. Dahle, "Modification of Al-Si alloys with Ba, Ca, Y and Yb", Journal of Light Metals, 1, 229 (2001).

상세보기
H. C. Lia, Y. Sun, and G. Sun, "Correlation between mechanical properties and amount of dendritic ${\alpha}$ -Al phase in as-cast near eutectic Al-11.6%Si alloys modified with strontium", Materials Science and Engineering: A, 335, 62 (2002).

상세보기
K. Nogita, S. D. Mcdonald, and K. A. Dahle, "Eutectic modification of Al-Si alloys with rare earth metals", Materials Transactions, 45, 323 (2004).

상세보기
C. Cui, A. Schulz, L. Achelis, V. Uhlenwinkel, H. Leopold, V. Piwek, Z.Tang, and T. Seefeld, "Development of low-melting-point filler materials for laser beam brazing of aluminum alloys", Mat.-wiss. u. Werkstofftech., 45(8), 717 (2014).

상세보기
T. I. Yoo, J. P. Jung, and Y. S. Shin, "Practical brazing technology", Engineering information, Seoul (2005).
A. Tressaud, "Functionalized Inorganic Fluorides", pp.214- 221, John Wiley & Sons Ltd., India (2010).
W. Dai, S. B. Xue, J. Y. Lou, Y. B. Lou, and S. Q. Wang, "Torch brazing 3003 aluminum alloy with Zn-Al filler metal", Transactions of nonferrous metals society of China, 22, 30 (2012).

상세보기
K. Allen, "Solving the problems inherent to torch brazing aluminum", Welding Journal, 39 (2009).
D. Claydon, and A. Sugihara, "Brazing aluminum automotive heat exchanger assemblies using a non-corrosive flux process", SAE technical paper, 830021 (1983).
W. E. Cooke, T. E. Wright, and J. A. Hirschfield, "Furnace brazing of aluminum with a non-corrosive flux", SAE technical paper, 780300 (1978).
M. P. Heisler, "Temperature chart for induction and constant heating", Trans. ASME., 69(3), 227 (1947).
V. Rudnev, D. Loveless, R. Cook, and M. Black, "Handbook of induction heating", Manufacturing Engineering and Materials Processing, 61, pp.80-98 (2003).
J. N. Antonevichm, "Fundamentals of ultrasonic soldering", Welding Journal, 55(7), 200 (1976).
M. Ding, P. I. Zhang, Z. Y. Zhang, and S. Yao, "Direct soldering 6061 aluminum alloys with ultrasonic coating", Ultrasonics Sonochemistry, 17, 292 (2010).

상세보기
M. Naka, and K. M. Hafez, "Applying of ultrasonic waves on brazing of alumina to copper using Zn-Al filler alloy", Journal of materials science, 38(16), 3491 (2003).

상세보기
J. Yan, Z. Xu, L. Shi, X. Ma, and S. Yang, "Ultrasonic assisted fabrication of particle reinforced bonds joining aluminum metal matrix composites", Materials and Design, 32(1), 343 (2011).

상세보기

저자의 다른 논문 :

LOADING...

표제어: PCR

동의어: Packet Collision Rate

용어 설명 출처 목록 (6)

용어 설명: PCR은 세균 특이성이 있는 primer를 이용하여 적은 수의 세균이 있을지라도 쉽게 검출할 수 있는 유용한 방법이며, 이를 이용하여 구강 내 치면세균막이나 타액에서 직접 세균을 검출할 수 있게 되었다[8].

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관 관리번호, 논문명, 대등논문명, 저자 , 저널/프로시딩명, 발행기관, 발행년, 발행언어, 권, 호, 시작페이지, 끝페이지, ISBN, ISSN, 주제분야, 키워드, 초록(한글), 초록(영문), 저자(소속기관)
저장형식	Text(ASCII format) Excel format RefWorks Direct Export RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증