NTIS 바로가기Intermetallics, v.15 no.5/6, 2007년, pp.639 - 643
Yao, K.F. (Division of Engineering Materials, Department of Mechanical Engineering, Tsinghua University, Beijing 100084, PR China) , Yang, Y.Q. , Chen, N.
In present work, Pd77.5Cu6Si16.5 bulk metallic glass balls with diameter up to 6mm have been prepared by fluxing and water quenching method. It has been found that the Pd-Cu-Si glassy alloy exhibits a compressive plastic strain of about 11.4%, together with strain hardening characteristics. A large ...
Appl Phys Lett Drehman 41 716 1982 10.1063/1.93645
Mater Trans JIM Zhang 32 1005 1991 10.2320/matertrans1989.32.1005
Appl Phys Lett Peker 63 2342 1993 10.1063/1.110520
Science Greer 267 1947 1995 10.1126/science.267.5206.1947
Nature Tang 402 160 1999 10.1038/45996
Acta Mater Inoue 48 279 2000 10.1016/S1359-6454(99)00300-6
MRS Bull Johnson 24 42 1999 10.1557/S0883769400053252
Mater Sci Eng R Wang 44 45 2004 10.1016/j.mser.2004.03.001
Appl Phys Lett Wang 84 4029 2004 10.1063/1.1751219
Acta Mater Xu 52 2621 2004 10.1016/j.actamat.2004.02.009
Chin Phys Lett Tang 21 901 2004 10.1088/0256-307X/21/5/039
Chin Phys Lett Yao 22 1481 2005 10.1088/0256-307X/22/6/051
Acta Metall Spaepen 25 407 1977 10.1016/0001-6160(77)90232-2
Acta Metall Argon 27 47 1983 10.1016/0001-6160(79)90055-5
Phys Rev Lett Das 94 205501 2005 10.1103/PhysRevLett.94.205501
Appl Phys Lett Yao 88 122106 2006 10.1063/1.2187516
Nature Chen 367 541 1994 10.1038/367541a0
Phys Rev Lett Schroers 93 255506 2004 10.1103/PhysRevLett.93.255506
Philos Mag Lett Inoue 85 221 2005 10.1080/09500830500197724
Mater Sci Eng Pampillo 13 181 1974 10.1016/0025-5416(74)90185-2
Phys Rev Lett Zhang 91 045505 2003 10.1103/PhysRevLett.91.045505
J Non-Cryst Solids Chen 18 157 1975 10.1016/0022-3093(75)90018-6
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.