NTIS 바로가기Ceramics international, v.40 no.6, 2014년, pp.7661 - 7667
The mechanical reliabilities of 99% alumina ceramics preformed by dry pressing using various pressures and reshaped by cold isostatic pressing (CIP) at 150MPa are investigated using the maximum likelihood method for the estimation of the Weibull parameters of the results. The results indicate that a...
Mechanics Research Communications Yang 31 429 2004 10.1016/j.mechrescom.2004.02.002 Relationship between refined Griffith criterion and power laws for cracking
J. Eur. Ceram. Soc. Shinohara 20 843 2000 10.1016/S0955-2219(99)00237-X Variation of the microstructure and fracture strength of cold isostatically pressed alumina ceramics with alteration of dewaxing procedures
Rare Metal Materials and Enqineering Meng 38 1178 2009 Weibull distribution of flexural strength of silica ceramics
J. Eur. Ceram. Soc. Seidel 17 727 1997 10.1016/S0955-2219(96)00084-2 Reliability of Alumina Ceramics. 2: Effect of Processing
Int. Journal of Refractory and Metals and Hard Materials Nevarez-Rascon 29 333 2011 10.1016/j.ijrmhm.2010.12.008 Compressive strength, hardness and fracture toughness of Al2O3 whiskers reinforced ZTA and ATZ nanocomposites: Weibull analysis
J. Eur. Ceram. Soc. Danzer 26 3043 2006 10.1016/j.jeurceramsoc.2005.08.021 Some notes on the correlation between fracture and defect statistics: Are Weibull statistics valid for very small specimens?
J. of the mechanical behavior of biomedical material Fan 8 21 2012 10.1016/j.jmbbm.2011.12.010 Part ?: Porosity dependence of the Weibull modulus for hydroxyapatite and other brittle materials
J. Eur. Ceram. Soc. Warren 21 335 2001 10.1016/S0955-2219(00)00183-7 Fracture of brittle materials: effects of test method and threshold stress on the Weibull modulus
J. Eur. Ceram. Soc. Papargyris 18 451 1998 10.1016/S0955-2219(97)00165-9 Estimator type and population size for estimating the Weibull modulus in ceramics
J. Eur. Ceram. Soc. Franken 19 1307 1999 10.1016/S0955-2219(98)00425-7 Weibull analysis of soldered MLC under bending load stress
Engineering Fracture Mechanics. Fok 68 1171 2001 10.1016/S0013-7944(01)00022-4 A numerical study on the application of the Weibull theory to brittle materials
Materials Science and Engineering A Hudak 528 8028 2011 10.1016/j.msea.2011.07.013 On comparing the shape parameters of two Weibull distributions
Computational Materials Science Stoyan 68 181 2013 10.1016/j.commatsci.2012.10.016 Back to and beyond Weibull-The hazard function approach
Ceramics Internatinal Defez 39 3329 2013 10.1016/j.ceramint.2012.10.022 Influence of the load application rate and the statistical model for brittle failure on the bending strength of extruded ceramics tiles
Journal of the Mechanical Behavior of Biomedical Materials Fan 2013 10.1016/j.jmbbm.2013.01.031 Weibull modulus and fracture strength of highly porous hydroxyapatite
Theoretical and Applied Fracture Mechanics. Saghafi 52 180 2009 10.1016/j.tafmec.2009.09.007 Improved linear regression method for estimating Weibull parameters
Chemical World Shang 346 1994 Preparation and indentification
X.Y. Li. Research on estimation for the three-parameter Weibull Distribution. Master Degree of Beijing Jiaotong University.
Int. J. Mech. Sci. Mori 40 989 1998 10.1016/S0020-7403(97)00144-6 Simulation of microscopic shrinkage behavior in sintering of powder compact
J. Eur. Ceram. Soc. Yu 19 2619 1999 10.1016/S0955-2219(99)00056-4 Arch effect in high isostatic pressure compacts
J. Eur. Ceram. Soc. Madjoubi 19 2957 1999 10.1016/S0955-2219(99)00087-4 Weibull statistical analysis of the mechanical strength of a glass eroded by sand blasting
J. Eur. Ceram. Soc. Prokhorov 17 129 1997 10.1016/S0955-2219(96)00153-7 Akimov. Cold isostatic pressing as a method of pre-forming green ceramic ware
Ceramics International. He 2013 10.1016/j.ceramint.2013.04.086 Numerical simulation of cold isostatic pressed alumina parts produced by selective laser sintering and part shape optimization
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.