$TiO_2$ hydrate coating on mica in an aqueous solution of $TiOSO_4$ by the hydrolysis using ammonia water studied with emphasis on coating conditions for a uniform coating. For the uniform coating of $TiO_2$ film on mica surface, it was found that smaller mica partic...

$TiO_2$ hydrate coating on mica in an aqueous solution of $TiOSO_4$ by the hydrolysis using ammonia water studied with emphasis on coating conditions for a uniform coating. For the uniform coating of $TiO_2$ film on mica surface, it was found that smaller mica particles were coated more uniformly compared to larger particles. It was necessary to suppress the rate of formation of hydrated $TiO_2$ particles in solution, which were deposited on mica and generate irregular coating. It was also necessary to control precipitation yield by varying the reaction temperature to obtain uniform coating. More uniform coating was obtained with higher precipitation yield. A uniform dense film was formed when mica particles of average size of $14.7{\mu}m$ is used for mica slurry solution, of which pH is 2.5, and the factor of acidity of $TiOSO_4$ solution is 291, and the solution was kept at $80^{\circ}C$ for 3 hours. The morphology of $TiO_2$ film formed on mica was little affected by firing at $900^{\circ}C$.