Melting behavior and bridge phenomenon of solder paste, which is essential for surface mount technology in pachaging, were investigated. Solder paste of Sn-37%Pb was printed on Cu-pattern of PCB, and heated over melting point. Melting behavior of the paste was observed using CCD-camera. In order to ...

Melting behavior and bridge phenomenon of solder paste, which is essential for surface mount technology in pachaging, were investigated. Solder paste of Sn-37%Pb was printed on Cu-pattern of PCB, and heated over melting point. Melting behavior of the paste was observed using CCD-camera. In order to modelize the melting and agglomeration phenomena of paste, two solder balls of 0.76 mm diameter were used. As experimental results, the paste start to melt from the margin of the printed shape. The height of the melted paste decreased from 270 $\mu\textrm{m}$ to 200 $\mu\textrm{m}$ firstly, and finally recovered to 250 $\mu\textrm{m}$ During the melting procedure, pores were evolved from the molted paste. Concerning melting model of solder ball, relationship between contact area of solder ball and soldering time was derived as $\chi^2/t=4r \; \gamma/\eta=7.56 m^2$/s at $280^{\circ}C$.

주제어