Abstract ▼ AI-Helper

Polyvinylidenefluoride and Polytetrafluoroethylene have been irradiated by 1 keV Ar+ ion beam in an $O_2$ environment. Hydrophilic functional groups (such as -(C-O)-,-(C=O)-,-(C=O)-O- and so on) were formed on fluoropolymers. Contact angles of water to PVDF were reduced from $75^{\ci...

Polyvinylidenefluoride and Polytetrafluoroethylene have been irradiated by 1 keV Ar+ ion beam in an $O_2$ environment. Hydrophilic functional groups (such as -(C-O)-,-(C=O)-,-(C=O)-O- and so on) were formed on fluoropolymers. Contact angles of water to PVDF were reduced from $75^{\circ}$ to $31^{\circ}$. Re-increase of contact angle was originated from carbonization phase in case of high dose irradiation above $1{\times}10^{16} Ar^+cm^2$. Contact angles to PTFE decreased at low dose irradiation and were exaggerated to about $140^{\circ}$ due to cone type surface at high dose irradiation. Hydrophilic functional groups have played an important role on adhesion between metal and fluoropolymers by acid-base interaction and chemical bond formation. Adhesion of Pt/PVDF was enhanced by acid-base interaction because Pt is inert metal. Chemical bond formation between Cu and PTFE could enlarge the adhesion strength of Cu/PTFE.