NTIS 바로가기한국세라믹학회지 = Journal of the Korean Ceramic Society, v.45 no.9 = no.316, 2008년, pp.549 - 555
허용석 (국민대학교 기계자동차공학부) , 박상현 (국민대학교 기계자동차공학부) , 한인섭 (한국에너지기술연구원 융복합재료연구센터) , 우상국 (한국에너지기술연구원 융복합재료연구센터) , 정연길 (창원대학교 나노신소재공학부) , 백운규 (한양대학교 신소재공학부) , 이기성 (국민대학교 기계자동차공학부)
The thermal barrier coating must withstand erosion when subjected to flowing gas and should also maintain good stability and mechanical properties while it must also protect the turbine component from high temperature, hot corrosion, creep, and oxidation during operation. In this study we investigat...
* AI 자동 식별 결과로 적합하지 않은 문장이 있을 수 있으니, 이용에 유의하시기 바랍니다.
J. R. Nicholls, K. J. Lawson, A. Johnstone, and D.S Rickerby, "Methods to Reduce the Thermal Conductivity of EBPVD TBCs," Surf. Coat. Tech., 150-151 383-91 (2002)
W. Beele, G. Marijnissen, and A. van Lieshout, "The Evolution of Thermal Barrier Coatings - Status and Upcoming Solutions for Today's Key Issues," Surf. Coat. Tech., 120- 121 61-7 (1999)
J. Toscano, R. Vaaen, A. Gil, M. Subanovic, D. Naumenko, L. Singheriser, and W. J. Quadakkers, "Parameters Affecting TGO Growth and Adherence on MCrAlY Bond Coats for TBC's," Surf. Coat. Tech., 201 3906-10 (2006)
S. Kramer, S. Faulhaber, M. Chambers, D. R. Clarke, C. G. Levi, J. W. Hutchinson, and A. G. Evans, "Mechanisms of Cracking and Delamination within Thick Thermal Barrier Systems in Aero-Engines Subject to Calcium-Magnesium- Alumino-Silicate(CMAS) Penetration," Mater. Sci. and Eng., A490 26-35 (2008)
N. G. bychkov, V. P. Lukash, Y. A. Nozhnitsky, A. V. Perchin, and A. D. Rekin, "Investigations of Thermomechanical Fatigue for Optimization of Design and Production Process Solutions for Gas-Turbine Engine Parts," International Journal of Fatigue., 30 305-12 (2008)
K. S. Lee, S. K. Lee, and D. K. Kim, "A Study on the Coating Fracture in Silicon Nitride Bilayer : I. Effect of Elastic/ Plastic Mismatch(in Korean)," J. Kor. Ceram. Soc., 34 [12] 1268-74 (1997)
K. S. Lee, S. K. Lee, and D. K. Kim, "A study on the Coating Fracture in Silicon Nitride Bilayer : II. Effect of Coating Thickness(in Korean)," J. Kor. Ceram. Soc., 35 [1] 48-54 (1997)
B. R. Lawn, "Indentation of Ceramic with Spheres: A Century after Hertz," J. Am. Ceram. Soc., 81 [8] 1997-94 (1998)
B. R. Lawn and T. R. Wilshaw, "Indentation Fracture : Principles and Applications," J. Mater. Sci., 10 [6] 1977-94 (1975)
F.B. Abudaia, J.T. Evans, and B.A. Shaw, "Spherical Indentation Fatigue Cracking," Mater. Sci. and Eng., A391 181- 87 (2005)
S.H. Park, S.K. Kim, T.W. Kim, U. Paik, and K.S. Lee, "Indentation on YSZ Thermal Barrier Coating Layers Deposited by Electron Beam PVD," Philosophical Magazine, 86 5453-63 (2006)
J. Y. Kwon, J. H. Lee, H. C. Kim, K. S. Lee, U. Paik, and Y. G. Jung, "Effect of Thermal Fatigue on Mechanical Characteristic and Contact Damage of Zirconia Based Thermal Barrier Coatings with HVOF-Sprayed Bond Coat," Mater. Sci. and Eng., A429 173-80 (2006)
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
저자가 APC(Article Processing Charge)를 지불한 논문에 한하여 자유로운 이용이 가능한, hybrid 저널에 출판된 논문
※ AI-Helper는 부적절한 답변을 할 수 있습니다.