NTIS 바로가기Composites. Part A, Applied science and manufacturing, v.38 no.3, 2007년, pp.785 - 794
de Morais, A.B. (University of Aveiro, Department of Mechanical Engineering, Campus Santiago, 3810-193 Aveiro, Portugal) , Pereira, A.B.
This paper describes an experimental study involving double cantilever beam (DCB), end-notched flexure (ENF) and four-point end-notched flexure (4ENF) tests on carbon/epoxy unidirectional specimens. The main purpose was to evaluate the so-called effective crack method (ECM), which avoids operator cr...
Brunner AJ, Blackman BRK, Davies P. A status report on delamination resistance testing of polymer-matrix composites. EUROMECH 473 Colloquium, Porto, October 27-29, 2005.
Compos Sci Technol Brunner 66 785 2006 10.1016/j.compscitech.2004.12.040 Calculating a damage parameter and bridging stress from GIc delamination tests on fibre composites
ASTM STP Corleto 1012 201 1989 Mode II delamination fracture toughness of unidirectional graphite/epoxy laminates
ASTM STP O’Brien 1330 3 1998 Composite interlaminar shear fracture toughness, GIIc: shear measurement or sheer myth
Compos Struct Wang 36 71 1996 10.1016/S0263-8223(96)00066-9 Use of the end-loaded split (ELS) test to study stable fracture behaviour of composites under mode II loading
Eng Fract Mech Blackman 72 877 2005 10.1016/j.engfracmech.2004.08.007 The determination of the mode II adhesive fracture resistance, GIIc, of structural adhesive joints: an effective crack length approach
Eng Fract Mech Blackman 73 2443 2006 10.1016/j.engfracmech.2006.05.022 Mode II fracture testing of composites: a new look at an old problem
De Moura MFSF, de Morais AB. Equivalent crack based analyses of ENF and ELS tests. EUROMECH 473 Colloquium, Porto, October 27-29, 2005.
Eng Fract Mech De Morais 72 2615 2005 10.1016/j.engfracmech.2005.05.003 Assessment of initiation criteria used in interlaminar fracture tests of composites
Eng Fract Mech De Morais 73 2264 2006 10.1016/j.engfracmech.2006.05.003 Evaluation of initiation criteria used in interlaminar fracture tests
Kageyama K, Kimpara I, Suzuki T, Ohsawa I, Kanai M, Tsuno H. Effects of test conditions on mode II interlaminar fracture toughness of four-point ENF specimens. Proceedings of ICCM-12, Paris, July 1999, p. 362-9.
J Reinf Plastics Compos Davidson 24 1611 2005 10.1177/0731684405050402 Effects of friction, geometry, and fixture compliance on the perceived toughness from three-and four-point bend end-notched flexure tests
Compos Sci Technol Williams 35 367 1989 10.1016/0266-3538(89)90058-4 End corrections for orthotropic DCB specimens
J Compos Technol Res Reeder 25 191 2003 Refinements to the mixed-mode bending test for delamination toughness
Compos Sci Technol Pereira 64 1653 2004 10.1016/j.compscitech.2003.12.001 Mode II interlaminar fracture of carbon/epoxy multidirectional laminates
Acta Metall Mater Spearing 40 2191 1992 10.1016/0956-7151(92)90137-4 The role of fiber bridging in the delamination resistance of fiber-reinforced composites
J Mech Phys Solids Suo 40 1 1992 10.1016/0022-5096(92)90198-B Delamination R-curve phenomena due to damage
Composites Part A Sorensen 29A 1443 1998 10.1016/S1359-835X(98)00025-6 Large-scale bridging in composites: R-curves and bridging laws
Plastics Rubber Compos Sorensen 29 119 2000 10.1179/146580100101540879 Crack growth in composites-Applicability of R-curves and bridging laws
Eng Fract Mech Tamuzs 68 513 2001 10.1016/S0013-7944(00)00131-4 Progressive delamination and fiber bridging modeling in double cantilever beam composite specimens
J Compos Mater Mi 32 1246 1998 10.1177/002199839803201401 Progressive delamination using interface elements
Mech Mater De Morais 35 641 2003 10.1016/S0167-6636(02)00289-2 Analysis of crack propagation in double cantilever beam tests of multidirectional laminates
J Compos Mater Camanho 37 1415 2003 10.1177/0021998303034505 Numerical simulation of mixed-mode progressive delamination in composite materials
Compos Sci Technol Li 65 537 2005 10.1016/j.compscitech.2004.08.004 Use of a cohesive-zone model to analyze the fracture of a fiber-reinforced polymer-matrix composite
Compos Sci Technol Sun 66 1297 2006 10.1016/j.compscitech.2005.10.013 Modeling of composite fracture using cohesive zone and bridging models
Eng Fract Mech Wang 71 219 2004 10.1016/S0013-7944(03)00096-1 Novel beam analysis of end notched flexure specimen for mode II fracture
Fracture mechanics testing methods for polymers, adhesives and composites. ESIS Publication 28. Moore DR, Pavan A, Williams JG. Elsevier Science, 2001.
Eng Fract Mech Rybicki 9 931 1977 10.1016/0013-7944(77)90013-3 A finite element calculation of stress intensity factors by a modified crack closure integral
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.