This study was attempted to investigate physicochemical properties, molecular structural properties of native and acid-treated chestnut starch and chestnut starch gel. The amylose content was 18.9% and X-ray diffraction pattern showed Cb type. Swelling power was increased abruptly in the range of

This study was attempted to investigate physicochemical properties, molecular structural properties of native and acid-treated chestnut starch and chestnut starch gel. The amylose content was 18.9% and X-ray diffraction pattern showed Cb type. Swelling power was increased abruptly in the range of $65^{\circ}C{\sim}75^{\circ}C$ but increased slowly after that and solubility was increased abruptly until $70^{\circ}C$ but increased slowly after that. In amylograms which have different heating temperatures, cooling viscosity at $50^{\circ}C$ was reduced as heating temperature was increased. In molecular structural properties of amylose, ${\lambda}_{max}$ was 640 nm, ${\beta}-amylolysis$ limit was 84.2% and the degree of polymerization was 951 and in those of amylopectin, ${\lambda}_{max}$ was 570 nm, ${\beta}-amylolysis$ limit was 58.2%, the degree of polymerization was 1371 and average chain length was 22.6. In gel chromatography elution profiles of starch and amylose, 4.0% and 11.5% of low molecular weight-molecules($<5{\times}10^5$) were leached out. In gel chromatography elution profiles of soluble starch, the higher heating temperature was, the more high molecular weight-starches were leached out. The elution profiles after debranching amylopectin with pullulanase showed 2.2 of the ratio of peakIII(DP 10-15) to peakII(DP 35-45). Acid hydrolysis extent of 2.2 N HCI-treated starch at $35^{\circ}C$ for 10 days was 96% and hydrolysis rate showed two step pattern which had border line at 4 days. In elution profiles of acid treated chestnut starch, amylopectin peak was disappeared compeletly after 6 hrs and converted short chains of DP 10-15. Amylose content was increased until 6 hrs but decreased after that. Hardness of starch gel made at $75^{\circ}C$ of heating temperature and cohesiveness of starch gel made at $85^{\circ}C$ of heating temperature were the highest. Retrogradation rate of starch gels were relatively high, especially for the starch gel made at $75^{\circ}C$ of heating temperature.

Keyword